Two component low odor acrylic AB structural adhesive, 801

SD801 is a two component low odor acrylic structural adhesive that produces a milder odor than traditional acrylic adhesives when applied. The operation time is 3-5 minutes, and the curing positioning is 5-10 minutes. It reaches the usable level after 1 hour. After complete curing, it has characteristics such as high shear, high peeling, and good impact resistance. Suitable for bonding most metals, ceramics, rubber, wood, etc. Temperature resistance range: -30~120 ℃.

 

Main characteristics of acrylic structural adhesive

Low odor and environmentally friendly, upgraded third-generation acrylate
Rapid curing and high strength
High shear, peel strength
The operation time is 5 minutes, the initial solidification is 15 minutes, and the usable strength is reached after 1 hour
Mainly used in: currency verification machines, tensile testing machines, fiber optic cables, couplings, USB drives, optical sensors, hydraulic couplers, 3D printers, speakers, underwater thrusters, magnetic drills

 

Executive standard for acrylic structural adhesive

Complies with GB 33372-2020 (VOC) volatile organic compound certification, REACH EU testing standards, and the enterprise has passed UL certification for flame retardancy grade E358706, ISO14001:2015 certification, ISO9001:2015 certification. The cited standard is HG/T3947-2007 single component room temperature vulcanization silicone adhesive/sealant, and has passed the national high-tech enterprise certification. Our products have passed 1000 hours of cold and hot impact testing, 1000 hours of dual 85 (high temperature and humidity) testing, and 1000 hours of high temperature aging testing, committed to providing reliable thermal conductivity solutions for industries such as automobiles, communication, and security.

 

Acrylate structural adhesive application industry

Digital electronics, office equipment, instruments, communication equipment, security equipment, electric tools

 

Performance of Acrylate Structural Adhesive

Acrylic AB adhesive

SD801

Appearance/Color

 light colour

Viscosity (mPa.s 25℃)

20000

proportion (g/ml 25℃)

 0.85-1.0

proportioning(by weightpbw)

     A:B=1:1

Initial solidification time

5-8 minutes

Fully cured

24hours

Temperature resistance range(℃)

   -40℃-110℃

Hardness (Shore D)

65

Seismic resistance (m2)

>16kJ

Peeling force (cm)

>70 N

Bonding of different materials

aluminium(mm2)

>18

iron(mm2)

>21

stainless steel(mm2)

>22

 

Usage and precautions

Equipped with an AB glue gun and thread mixing head, the glue can be applied. The thickness of the adhesive layer should preferably be 0.05mm. The adhesive after application should be immediately assembled and tightly clamped, and uniform contact pressure will ensure maximum bonding strength. To achieve the highest mechanical strength, the material surface can be polished or sandblasted, and then the surface dust and oil stains can be wiped with a special solvent. It is necessary to apply adhesive on both sides of the bonding area, and then fix the bonding area to avoid misalignment. Do not cross the caps of AB and AB to prevent contamination of the original adhesive.

 

Precautions for Acrylate Structural Adhesive

This product has a slightly irritating odor. Please wear a gas mask and anti-corrosion gloves when operating.
Cover at any time after each material collection to avoid moisture absorption affecting curing and performance.
Use this product extensively in a well ventilated area.

 

Packaging and preservation

This product is packaged in AB mixed tube, 64g/piece. It is transported as a non hazardous material and should be stored in a dry and cool place (below 5 ℃~26 ℃). The shelf life of this product is within 12 months from the date of manufacture.

Product description


Key words:

Related products

undefined

undefined

Get free product quotes

Our staff will contact you within 24 hours (weekdays), if you need other services, please call the service hotline: 0752-6822862
%{tishi_zhanwei}%